Modelo: various
Product Use: 1: Glue-coating before glue coping withered material surface cleaning, clean before coating. Otherwise, it will affect the adhesive seal. 2: Takes out A and B two components according to 10: 1 proportion to carry on the mix agitation to be even, achieves the achromatism. 3: Manual or mechanical operation must arrange a direction coating and put some pressure, prevent the air wrapped into. 4: Construction of the ambient temperature maintained at above 5 ° C |
Packaging into large, medium and small 1, large package: Group A[300KG] Group B [33.3KG] 2, medium package: Group A[30KG] Group B[3.35KG] 3, small package: Group A[4.5KG × 5 barrels of group B were] Group B[0.5KG × 5] |
Product features 1, Has a good weather ability, durability, use a long time no cracks; 2,To the sealed components it has fully stable adhesion and durable adhesion, coagulation in water soil have long-term adhesion; 3,Water vapor transmittance is extremely low, the two-component polysulfide sealant has very good waterproof function; 4,Against fungi, best bacteria resistance; 5,Good construction work, the two-component polysulfide sealant can be fill into the joint very good. 6. no produce pollution for the sealing structure, no corrosion, and the two-component polysulfide sealant has no harm to human body. |
Under the conditions of the 23±2 °C and the R.H. 50±5% | ||||||
Item | Component A | Component B | ||||
Viscosity(Pa's) | 4000 | 800 | ||||
Appearance | Fine, smooth and homogeneous | fine, smooth and grease-like | ||||
Color | White | Black | ||||
Density(g/em 3 ) | 1.75±0.1 | 1.52±0.1 | ||||
Mixed Component A and Component B at 10:1 by weight, under the conditions of 23±2 °C and the R.H. of 50±5% | ||||||
Item | Standard | Result | Test method | |||
Resistance to flow, mm | Vertical | ≤3 | 0.8 | GB/T 1 13477 | ||
Level | No distortion | No distortion | ||||
Application Time, 30min ,S | ≤10 | 4.8 | ||||
A:B=10:1, Under the conditions of the 23±2 °C and the R.H. of 50±5%, after 7days of curing: | ||||||
Item | Standard | Result | Test method | |||
Durometer hardness (Shore A) | 45 | GB/T 1 531 | ||||
Tensile strength , MPa | MPa | 0.8 | GB/T 1 13477 | |||
Permeation rate of evaporation (g/m 2 .d) | ≤15 | 8 | GB/T 1 1037 | |||
GB/T 1 13477 | 25HM | JC/T 1 486 |
Grupos de Producto : Sellador impermeable serie > Sellador de polusulfuro