|Product Use: |
1: Glue-coating before glue coping withered material surface cleaning, clean before coating. Otherwise, it will affect the adhesive seal.
2: Takes out A and B two components according to 10: 1 proportion to carry on the mix agitation to be even, achieves the achromatism.
3: Manual or mechanical operation must arrange a direction coating and put some pressure, prevent the air wrapped into.
4: Construction of the ambient temperature maintained at above 5 ° C
|Packaging into large, medium and small|
1, large package: Group A[300KG] Group B [33.3KG]
2, medium package: Group A[30KG] Group B[3.35KG]
3, small package: Group A[4.5KG × 5 barrels of group B were] Group B[0.5KG × 5]
| Product features|
1, Has a good weather ability, durability, use a long time no cracks;
2,To the sealed components it has fully stable adhesion and durable adhesion, coagulation in water soil have long-term adhesion;
3,Water vapor transmittance is extremely low, the two-component polysulfide sealant has very good waterproof function;
4,Against fungi, best bacteria resistance;
5,Good construction work, the two-component polysulfide sealant can be fill into the joint very good.
6. no produce pollution for the sealing structure, no corrosion, and the two-component polysulfide sealant has no harm to human body.
|Under the conditions of the 23±2 °C and the R.H. 50±5%|
|Item||Component A||Component B|
|Appearance||Fine, smooth and homogeneous||fine, smooth and grease-like|
|Density(g/em 3 )||1.75±0.1||1.52±0.1|
|Mixed Component A and Component B at 10:1 by weight, under the conditions of 23±2 °C and the R.H. of 50±5%|
|Resistance to flow, mm||Vertical||≤3||0.8||GB/T 1 13477|
|Level||No distortion||No distortion|
|Application Time, 30min ,S||≤10||4.8|
|A:B=10:1, Under the conditions of the 23±2 °C and the R.H. of 50±5%, after 7days of curing:|
|Durometer hardness (Shore A)||45||GB/T 1 531|
|Tensile strength , MPa||MPa||0.8||GB/T 1 13477|
|Permeation rate of evaporation (g/m 2 .d)||≤15||8||GB/T 1 1037|
|GB/T 1 13477||25HM||JC/T 1 486|